Optically UV Clear Hard Coat

Product Detail

ICAL UV CLEAR HARD COAT

products are 100% solid content UV hard coating solution.  They have excellent scratch resistance and chemical resistance properties.  The products are suitable for various substrates such as PET, TAC, PC, PMMA and others. Recommended dry film thickness is 2-5µm.  Product can be coated directly or coated after diluting with solvents.  Products contain a complete formulation including oligomer, monomer, and photo initiators, and are ready to use. Since curing condition (UV light, temperature, curing speed) and equipment setup may vary, a fine-tuning is needed in order to achieve a maximum performance.  

Product Code	Product Description	Film        Thickness (µm)	Viscosity        (cps)	Pencil hardness (750g, H)	Adhesion	Appearance	Steel wool (0000#,X10)
UC-935	High pencil hardness, scratch resistance, good chemical and alkali resistance	4-6	3500	4	5B	Clear	No Scratch
UC-938	Balanced property and economic version with excellent performance.	2-4	3000	2-3	5B	Clear	Good
UC-945	Excellent outdoor weathering capability, Easy to clean, high pencil hardness, scratch resistance.	3-5	3000	3-4	5B	Clear	No Scratch
UC-845	Easy to clean, strong water repelling property, high pencil hardness, scratch resistance	3-5	3000	3-4	5B	Opaque	No Scratch
UC-835	High pencil hardness, scratch resistance, good chemical and alkali resistance	4-6	3500	4	5B	Opaque	No Scratch
UC-838	Superior scratch resistance, balanced property,  economic version with excellent performance.	3-5	3000	2-3	5B	Opaque	No Scratch
UC-910	Effectively blocking near UV region  (385-420nm), high pencil hardness, scratch resistance.	3-6	3500	4	5B	Brown liquid	No Scratch
UC-960	Excellent adhesion on both metal and oil based inks	3-6	800	2	5B	Clear	No Scratch
Curing Condition and Handling	Compatible with common organic solvents such as toluene, n-butyl acetate, ethyl acetate, acetone. Suggested mixing ratio, 2:1. All surfaces in contact with the material should be clean and free from flux residue, grease, or other contaminants prior to dispensing the material. Cure speed is dependent upon many variables, including lamp intensity, distance from the light source, required depth of cure, coating thickness and amount of material in shadowed areas Surfaces exposed to air may require higher intensity UV light to produce a harder surface cure. Parts should be allowed to cool after cure before testing and subjecting to any loads or electrical testing.
Note: * 1 kg of test conditions, 2000 times, film thickness 6 microns










Established in 2010, Namei Material Technology has been one of the leading optically uv clear hard coat manufacturers and suppliers in China through years' development. Under strict quality control and management system, we're able to offer you high-quality, eco-friendly, GOTS approved and VOC free optically uv clear hard coat at competitive price. Now take action to contact us.